An aluminium finish with the look of natural wood.
Consists of an aluminium base with a wood effect finish. Special inks are used which, when heated, adhere to the material and produce the same effect as wood grain. Thanks to this process we achieve this finish on aluminium with all the advantages of durability, maintenance and protection offered by lacquering and without the disadvantages of wood. This technique is highly resistant and has greater durability than other materials.
Protect surfaces during handling and rinse immediately with plenty of clean water if exposed to acids or alkalis. Clean regularly using lukewarm water, a neutral pH detergent, and a soft non-abrasive cloth or sponge, especially in coastal or industrial areas. Avoid abrasive materials, strong chemicals, solvents, and cleaning on hot surfaces above 25°C. Do not allow dirt, moisture, soil, water, or concrete residue to remain on the surface.
Baking time / temperature
Min: 24 to 150 °C / 75,2 to 302 °F - Max: 26 to 150 °C / 78,8 to 302 °F
Gloss at 60º angle
Min: 6 - Max: 9 ISO 2813
Direct impact 12.5 mm
30 ISO 2813
Indirect impact 12.5 mm
30 ISO 2813
Cross-cut adhesion
0 ISO 2813
Erichsen Cupping test
Min: 5 - Max: 11 ISO 2813
Bend test (Cylindrical Mandrel)
6 ISO 2813
Avg. Particle size
Min: 50 - Max: 55
Particle size % < 100 MICRONS
Min: 80 - Max: 95
Particle size % < 50 MICRONS
Min: 50 - Max: 65
Particle size % < 10 MICRONS
Min: 4 - Max: 8
Delta E colour
Visual, CIELAB Method
General appearance
Textured, NIZI-001 Method